SPECIAL SOLUTIONS – 4″ support caster GCM 42 PER – PL
Load capacity up to 800Kg
RIG
Reinforced without central pin, with single hardened and guarded ball raceway. Bolted wheel axle.
Wheel
C – Celeron Hardness: 103 Rockwell M. (-30°C to +120°C).
Manufactured with a compound obtained from macerated cotton fibers drenched with phenolic resin, molded by heat and pressure. They have excellent mechanical properties, are light and rugged, resistant to deformation under static loads and roll easily. They can be used over a wide temperature range. They are resistant to mild oils, greases and acids in low concentrations. Not recommended for applications in wet environments in contact with alkaline substances. (e.g., caustic soda, chlorine, cleaning products, soap and detergent). Nominal working speed is up to 4km/h.
Load capacity up to 400Kg
RIG
Reinforced without central pin, with single hardened and guarded ball raceway. Bolted wheel axle.
Wheel
BP – Thermoplastic Compound with PVC. Hardness: 80 Shore A. (-10°C to +50°C).
Produced with recyclable thermoplastic compound with PVC tread and polypropylene copolymer wheel center. They offer a soft and quiet rolling, great floor protection, good chemical, wear and impact resistance, resulting in an excellent cost-benefit ratio. Nominal working speed is up to 4km/h.
Capacity up to 450Kg
RIG
Reinforced without central pin, with single hardened and guarded ball raceway. Bolted wheel axle.
Wheel
B – Molded Rubber. Hardness: 80 Shore A. (-20°C to +70°C).
Produced with molded vulcanized rubber tread over a grey cast iron wheel center. They roll softly with a low noise level, absorb shocks and vibrations. They are resistant to abrasion and chemicals. They can be used at a speed of up to 20km/h when mounted with ball bearings.
Load capacity up to 1000Kg
RIG
Reinforced rig, made of stamped steel plate and swivel head with double ball raceway, zinc-plated finish. Bolted wheel axle.
Wheel
C – Celeron Hardness: 103 Rockwell M. (-30°C to +120°C).
Manufactured with a compound obtained from macerated cotton fibers drenched with phenolic resin, molded by heat and pressure. They have excellent mechanical properties, are light and rugged, resistant to deformation under static loads and roll easily. They can be used over a wide temperature range. They are resistant to mild oils, greases and acids in low concentrations. Not recommended for applications in wet environments in contact with alkaline substances. (e.g., caustic soda, chlorine, cleaning products, soap and detergent). Nominal working speed is up to 4km/h.